07/12/2007 07:34 514-932-2072 PIERREXPERT INC PAGE 06 <br /> 8810 Place Turcot Montmal(Quebec)Canada HSC 1W3 <br /> Tel:514-9324642 Fax:5 14-932-2072 <br /> STONEMATE SPECIFICATION <br /> TECHNICAL DATA <br /> Basic Material Silyl modified polymer <br /> (SMP) <br /> Curing method Moisture <br /> Specific gravity Ca. 1.4 g/ml <br /> Skin forming time Ca. 10 min. (70°F/20°C @50% R.H.) <br /> Open time <15 min. (707/20°C @50% R.H.) <br /> Curing speed after 24 hrs Ca.3 mm (70°F/200C @50% R.H.) <br /> Shore a hardness Ca.65 (DIN 53505) <br /> Volume change <3% (DIN 5245 1) <br /> Green strength Ca. 1800 Pa (Physical rheometer MC 100) <br /> (Maximum load which can be applied per mt uncured adhesive without sagging) <br /> Electrical volume resistivity >1011 Vem (DIN53482) <br /> Tensile stress(100%) 300 psa(ca.2.1 MPa) (DIN 53504/ISO 37) <br /> Tensile stress at break 420 psi(ca.2.9 MPa) (DIN 53504/)SO 37) <br /> Elongation at break Ca.225% (DIN 53504/ISO 37) <br /> Shear stress 360 psi(ca.2.5 MPa) (DIN 53283/ASTM D1002) <br /> (Aluminum-to-Aluminum;adhesive thickness 2mm,test speed 50 mm/min.) <br /> Tear propagation Ca. 13 N/mm (DIN 53515ASO 34) <br /> (Type C,test speed 500 mm/ndn.) <br /> E-modulus(10%) 623 psi (ca. 4.3 MPa) (DIN 53504/1S0 37) <br /> Solvent percentage 0% <br /> Isocyanate percentage 0% <br /> Temperature resistance 40°F to 212°F(-400C to+120°C) <br /> Temperature resistance 356°F (+180°C) (max 1/2 hr) <br /> Application temperature 41 OF to 95°F (+5°C to+35°C) <br /> UV and weather resistance Very good <br /> Color Black <br /> Packaging(Note;Sim subject to Stonemate 20 oz.sausage, 5 gallon pail, 52 gallon drum <br /> Chose) <br /> STORAGE STABILITY <br /> Stonemate may be stored for 12 months in a closed(unopened)container in a dry place at <br /> temperatures between 41°F to 86°F (5°C to 30°C) (cartridges 18 months). <br /> SAEETY PRECAUTIONS <br /> No specific precautions required. Consult safety data sheet. <br /> TRANSPORT CLASSIFICATION <br /> Not applicable. <br /> Paee 1 sur 1 <br />